Preparation of titanium machining process in the rough

       Titanium is a very active metal elements, and can effect all the elements, titanium during heating, can interact and oxygen, the oxide film formed on the surface. At different heating temperatures, the structure and properties of the oxide film is different. Thermoforming titanium complex, each batch is different mechanical properties, in order to ensure the quality of materials, manufacturers are available certificate and test report.
       1. Preparation of titanium raw material supply state requirements
       A titanium plate deformation - in metallurgy factory rolled into sheets of poor performance repeatability. Domestic and foreign production of titanium same composition, mechanical properties of the difference is not small; domestic different sheet metal factory production, performance is not the same, even if a plant product, different furnace number of its mechanical properties are not the same. Therefore, in order to ensure the quality of the parts, you should first make sure that the quality of raw materials. Treasury requisitioned from titanium and titanium sheet, should be equipped with the manufacturer factory certification and factory re-inspection certificate. In order to facilitate future verification, certification should be saved. When necessary, the basic situation of each plant can manufacture sheet metal parts to make records to future reference.
       All the plates were annealed condition require supply. To ensure the quality of the parts should be removed oxide and other pollutants plate surface. Titanium surface may not have cracks, peeling, crimping, inclusions and other defects, as well as through the traces of pickling. Sheet should be straight and wrapping paper out of the library. In the material after forming, assembly, transport and storage process, should be taken to prevent surface scratches.
       2, titanium rough cutting
       Wool preparation methods used in a variety of sheet metal parts, there are many similarities. Since the titanium plate thickness generally used in less than 2 mm, and a thickness of 1.5 mm or more parts so few titanium plate cutting can utilize existing equipment at room temperature.
       When cutting, should pay attention to try to make the edges smooth wool, particularly to prevent the edges of cracks, bite wounds and cut marks and other defects, in the cut planks should pay attention.
       Before forming wool deburring and removal should be sharp edges. Because of the sensitivity of titanium crack growth is strong, this work is extremely important, in order to eliminate the stress concentration to prevent cracking and scratches wool die during forming. Available cutting and filing, or sandpaper belt grinding deburring or polish.
       It should be noted that regardless of which method is used under the material, when crossed, only use non-polluting ink and pen, is not allowed to play in the wool stamp, offset or specially equipped only play tag.
       3, before forming degreasing and cleaning
       Before any thermoforming, should remove surface grease, or other contaminants, in order to avoid contamination of the titanium produced when heated. In addition, the surface of the oxide wool reduces plastic material, should be removed prior to forming. Therefore, in order to reduce the impact of various types of atmosphere environment, generally using a vacuum hardening furnace and vacuum annealing furnace heating, vacuum furnace inert gas can protect titanium and titanium alloy materials in the heating process from contamination.