Titanium forming mode

Cold Forming: plasticity in reply below the temperature of formation, deformation hardening process will occur, it will help improve strength and surface quality of the metal for the manufacture of semi-finished products.
Thermoforming: plasticity performed above the recrystallization temperature molding, hardening during deformation have both recrystallization, and hardening was recrystallized completely eliminated. Mechanical performance, small deformation force, large deformation or semi-finished products for the manufacture of wool culture.
Warm Forming: above and below the recrystallization temperature reply within a temperature range of plastic molding, there is hardening agent recovery phenomenon, but no recrystallization. High strength, poor semi-finished plastic parts or semi-manufactured for.
Cold forming: In general, Titanium sheet metal is used only for cold forming molded shape and deformation of simple uncomplicated words, such as pillars, gusset and gentle curvature of the skin, such as profiles. Singles of small sheet metal parts common cold roll forming a radian; hyperbolic degree gentle skin temperature can be used under the usual skin stretch forming machine forming.